A. Low voteji kutchinjiriza zakuthupi
1.1 chilinganizo
Epoxy utomoni E-44 100
Diluent Dibromophenyl glycidyl ether 20
Lawi retardant antimony trioxide 10
Yogwira silika ufa 400 mesh 200
Wothandizira 593
Diethylenetriamine 3
1.2 Njira yopangira
1.2.1 Youma pakachitsulo ufa kuti chinyezi pansipa 0.2%
1.2.2 onjezani utomoni wa epoxy, wocheperako, lawi lamoto, ndi ufa wa silicon ku riyakitala motere
1.2.3 kwezani kutentha kwa 100 ℃, degas osakaniza pansi -0.1Mpa zingalowe kwa 30min kuti pachilichonse
1.2.4 Wozizira mpaka pansi pa 50 ° C, onjezerani othandizira, sungani kutentha kosapitirira 50 ° C, digiri ya vacas degree -0.1Mpa, nthawi yosakanikirana yoposa 30min, kenako lowetsani.
B. Mkulu voteji ndi otsika voteji zipangizo kutchinjiriza
2.1 Kukhazikitsa
Epoxy utomoni E-44 100
Diluent Dibromophenyl glycidyl ether 20
Lawi retardant antimony trioxide 10
Yogwira silika ufa 400 mesh 300
Ochiritsa wothandizila S101 95
Accelerator DMP-30 1.5
2.2 Kupanga
2.2.1 Ufa wa silicon wouma mpaka chinyezi pansipa 0.2%
2.2.2 Pangani zigawo ziwiri motere
A chigawo epoxy utomoni, accelerator, lawi wamtundu uliwonse, pakachitsulo ufa 200
Wothandizira kuchiritsa kwa B, wocheperako, silicon ufa 100
2.2.3 Chigawochi chimatenthedwa mpaka 80-100 ℃, ndipo chisakanizocho chimachotsedwa pansi pa -0.1Mpa chopumira cha 30min kuti chikhale chofanana
2.2.4 Kutentha kwa chigawo B kumakwezedwa mpaka 50 ℃, ndipo chisakanizo chimachotsedwa pansi pa -0.1Mpa chopumira cha 30min kuti chikhale chofanana
2.2.5 Kuzizira mpaka pansi pa 50 ℃, onjezerani gawo A kupita ku chigawo B, sungani kutentha kosapitirira 50 ℃, digiri yopumira ya-degree -0.1Mpa, nthawi yosakanikirana 30min, mutha kulowa kuthira.