A. Minimum Nulla materia voltage
FORMULA 1,1
XLIV epoxy resinae E-C
Aut XX Diluent Dibromophenyl glycidyl
Misy cocti X flamma retardant trioxide
Silica Active pulveris reticulum CC CD
DXCIII XXV agente sanantes
III Diethylenetriamine
Productio processus 1,2
1.2.1 materies silicea natura Arida ad humorem content pulveris infra 0.2%
1.2.2 Adaugeo epoxy resinam, tenuior, flamma retardant, siliconisque pulveris reactor in sequentibus ad ordinem
1.2.3 C ad caliditatem ℃, Degas mixtisque de 30min ad conformitatem in vacuum -0.1Mpa
Frigus ut infra
1.2.4 L ° C, adde quaeque medendi agente, ut ad temperatus non magis quam L ° C, Degas vacuum -0.1Mpa gradu: tempus non magis quam 30min miscentes, tunc intrare casting processus.
High et humilis voltage B. Nulla materiae voltage
2.1 Silo
XLIV epoxy resinae E-C
Aut XX Diluent Dibromophenyl glycidyl
Misy cocti X flamma retardant trioxide
Silica Active pulveris CD reticulum CCC
XCV sanantes agente S101
Xi, 1.5 XXX propero
Productio processus 2,2
2.2.1 materies silicea natura Arida ad humorem content pulveris infra 0.2%
222 Fac duos argumentum curent in hoc ordine
A pars epoxy resinam, accelerator, flamma retardant, Pii pulveris CC
B curatio pars agente tenuioresque atque pulveris C Silicon
2.2.3 A est pars 80-100 ℃ calida est, et rudicula degassed -0.1Mpa in vacuum 30min ad uniformitatem
2.2.4 Ea sic temperanda est pars erexit ad L ℃ B, et rudicula degassed -0.1Mpa in vacuum 30min ad uniformitatem
Frigus ut infra 2.2.5 L ℃, pars addere pars A ad B, ut ad temperatus non magis quam L ℃, Degas gradus -0.1Mpa vacui: 30min miscentes tempore, vos potest intrare infundebat.