A. Obere ihe mkpuchi mkpuchi ihe
1.1 ulakpụrụ
Epoxy resin E-44 100
Diluent Dibromophenyl glycidyl ether 20
Ire ọkụ retardant antimony trioxide 10
Silica ntụ ntụ na-arụ ọrụ 400 mesh 200
onye na-agwọ ọrịa 593 25
Diethylenetriamine 3
1.2 Production usoro
1.2.1 Akọrọ silicon ntụ ntụ na mmiri ọdịnaya n'okpuru 0.2%
1.2.2 Tinye epoxy resin, mkpa, ire ọkụ retardant, na sịlịkọn ntụ ntụ na chernobyl na-eso iji
1.2.3 Bilie okpomọkụ na 100 ℃, degas ngwakọta n'okpuru -0.1Mpa agụụ maka 30min ka Ime Otu
1.2.4 Jụụ n'okpuru 50 Celsius C, gbakwunye ndị na-agwọ ọrịa, debe ọnọdụ okpomọkụ karịa 50 Celsius C, degas agụụ degree -0.1Mpa, agwakọta oge karịa 30min, wee banye usoro mgbatị ahụ.
B. High voltaji na ala voltaji mkpuchi ihe
2.1 Nhazi
Epoxy resin E-44 100
Diluent Dibromophenyl glycidyl ether 20
Ire ọkụ retardant antimony trioxide 10
Silica ntụ ntụ na-arụ ọrụ 400 mesh 300
onye na-agwọ ọrịa S101 95
DMP ome osooso-30 1.5
2.2 Production usoro
2.2.1 Akọrọ silicon ntụ ntụ na mmiri ọdịnaya n'okpuru 0.2%
2.2.2 Mee uzo abuo n’ime usoro a
Otu ihe na-eme epoxy resin, ome osooso, ire ọkụ retardant, silicon ntụ ntụ 200
B akụrụngwa na-agwọ ọrịa, thinner, sịlịkọn ntụ ntụ 100
2.2.3 The akụrụngwa ewe iwe 80-100 ℃, na ngwakọta na-degassed n'okpuru -0.1Mpa agụụ nke 30min ka Ime Otu
2.2.4 A na-ebuli ọnọdụ okpomọkụ nke akụrụngwa B ruo 50 ℃, ma agwakọta ya n'okpuru -0.1Mpa agụụ maka 30min na ịdị n'otu
2.2.5 Jụụ n'okpuru 50 ℃, gbakwunye mpaghara A na akụrụngwa B, debe ọnọdụ okpomọkụ karịa 50 ℃, degas agụụ degree -0.1Mpa, agwakọta oge 30min, ị nwere ike tinye agbapụtara.